chlorinated polyethylene cpe 135A

CPE 135A 1.Chlorinated Polyethylene(CPE) 2. fire-resistance 3. impact-resistance 4.It's widely used for hard PVC products

CPE 135A IMPACT MODIFIER OF HARD PVC

 

I Product features 

This product has good comprehensive physical properties such as fine Low-temperature toughness, high tensile strength, good compatibility with PVC. Under the right processing condition, it can form three-dimensional network with hard PVC, so it can give the product fine impact strength in low-temperature

II the key technical indexes

No	Item	Unit	Index	Test method
1	Chlorine Content	%	35±1	GB/T 7139
2	Density	g/cm3	≥0.5
3	Volatile Matter	%	≤0.3	GB/T 2914
4	Thermal Decomposition Temperature	°C	≥165	GB/T 2704
5	Crystallization residual(Ca)	%	≤2	DSC
6	SHORE Hardness(A)		≤57	GB/T 2411
7	Tensile strength	Mpa	≥9	GB/T 528
8	Screening Rate at 32 meshes	%	≥99	GB/T 2916

III Application

This product is suitable in PVC door and window; water pipe; cable pipe, PVC foam plate, PVC extruding plate and PVC press plate, etc.

 

IV Recommended ingredients

	Heterotype material for doors and windows		U-PVC Cess-pipe	U-PVC Cold bending pipe
PVC	100	100		100
CPE135A	8	4-6		10-15
Lead sulphosphare	1.5-2	1-1.5		1-1.5
Lead sulphate	4.0-4.5	3.0-3.5		3.0-3.5
Leda stearate	0.5-1	0.3-0.5		0.3-0.5
Calcium stearate	0.3-0.5	0.2		0.2
ACR 401	1.0-1.8	1.0-1.5		1.0-1.5
Light calcium carbonate	4-6	20-80		20-40
Rutile typify titanium pigment	4-5
Polyethylene wax	0.2-0.5	0.2-0.4		0.2-0.4
Paraffin	0.2-0.3	0.2-0.3		0.2-0.3
Stearic acid	0.2—0.4	0.5-0.8		0.5-0.8

Note:

1. The above ingredients are suitable for twin screw one-time extrusion molding.

2. The users have different process equipment, craft and condition, so the above ingredients are only for reference.

3. Our company can design the ingredients for customers.

chlorinated polyethylene cpe 135A